what are the causes of delayed fracture in case hardened steels?
- 4 Answers
- 7304 Views
- I also Faced
- E-Mail Answers
Answers were Sorted based on User's Feedback
Answer / hardik
case hardened steel has hard case (SURFACE) & though core
that wise it delayed
| Is This Answer Correct ? | 9 Yes | 3 No |
Answer / siva varun
case hardened steels have compressive residual stress on the
surface which tries to close the crack resulting in delayed
fracture.
| Is This Answer Correct ? | 7 Yes | 2 No |
Answer / venkat chilla
1.Due to high compressive stress on the surface and very
hard surface the neck or crack propagation on the surface is
delayed during deformation. In general the crack will be
initiated at the core of the material in normal tensile
loading at the region of internal defects and inter metallic
particles. on further increasing the load the crack will
propagate further towards out side of the surface. As the
surface is hard the crack propagation will be stoped by this
hard case and causes to delayed failure .
2. While in fatigue loading the crack will initiate at the
surface and propagate later in to core. As the hardened
surface is not allowed to initiate a crack and so delayed
failure.
| Is This Answer Correct ? | 5 Yes | 0 No |
sir.I am OBC candidate,recieved scholarship/freeship during academic year 2011-2012,2012-2013(my yearly income was below 4.5 lakh).my yearly income during academic year 2013-2014 was above 4.5 lakh.should I get scholarship/freeship in academic year 2013-2014 ?
How gold can be separated from mercury?
Define what is the different between ferrite percentage and ferrite number?
Define what metal cord transfers electricity?
how would you find out the type of stailess steel that has been used to make your dish?
What kind of shell systems are used for investment casting?
i want to go to US for Bachlore of computer science, I didn't appeared for SAT. my ielts scores are too low only 5.5 band and I am confused if VISA OFFICERS will ask why u hadn't given SAT. what i have to answer pl suggest?
carbon-3.23%,manganese-0.60%,silicon-2.25%,sulphur-0.086% phosphorus-0.122%,chromium-0.04%,nickel-0.10%, molybdenum-trace. WHAT IS THE GRADE OF THIS CAST IORN.
Why are the superalloys sometimes subjected to secondary melting processes?
What is the metallurgy use? What is the casting and forging?
On which basis annealing cycle of steel bars of UpTo 6 MTR can be decided.we r charging 40-45 metric ton load for annealing in bogie furnace?
what are the causes of scaling in cast iron, after subjecting it to annealing process.
-
Civil Engineering (5086) - Mechanical Engineering (4456)
- Electrical Engineering (16639)
- Electronics Communications (3918)
- Chemical Engineering (1095)
- Aeronautical Engineering (239)
- Bio Engineering (96)
- Metallurgy (361)
- Industrial Engineering (259)
- Instrumentation (3014)
- Automobile Engineering (332)
- Mechatronics Engineering (97)
- Marine Engineering (124)
- Power Plant Engineering (172)
- Textile Engineering (575)
- Production Engineering (25)
- Satellite Systems Engineering (106)
- Engineering AllOther (1379)