Answer / ajay kumar singh

C%=2.90-3.10
Mn%=0.60-1.00
si%=1.50-1.90
S%=0.10
P%=0.15
Cr%=0.30
Mo%=0.30
Cu%=0.25
All depend on casting object thickness, casting method and
required machinability rate so that material can not get
chilled

Answer / lahbib@allinterview.com

c: 3 % max
si 1.5-1.6 after inoculation
Mn 0.7-0.9
cr 0.3
Ni 0.5
S < 0.02
P <0.04

Why are the superalloys sometimes subjected to secondary melting processes?

1 Answers  

---

Do you know what metal might be considered the "most environmental"? I say aluminum because it can be recycled others on my team say brass.

0 Answers  

---

Explain proeutectoid ferrite

1 Answers  

---

How would a salt and water solution clean a penny but a vinegar and salt solution will not clean a penny? What is the cause of this?

0 Answers  

---

Why is chromium molybdenum steels used to build pressure vessels? Define what is special about the properties of chromium molybdenum steels that make them ideal for pressure vessels?

0 Answers  

---

what is the metallurgy use?

0 Answers  

---

carbon-3.23%,manganese-0.60%,silicon-2.25%,sulphur-0.086% phosphorus-0.122%,chromium-0.04%,nickle-0.10% molybdenum-trace. what is the grade of the above composition cast iron

0 Answers  

---

What is duplex and super duplex steel?

0 Answers  

---

What is the melting point of brass?

0 Answers  

---

The Hardness of wheel(or)grade of wheel refers to the

0 Answers   NIC,

---

Define what is the strongest metal?

0 Answers  

---

What is a cryogenic fluid?

0 Answers   Essar,

---