Question 48 - Let a ^ 2 = a x a and a ^ 3 = a x a x a where ^ is power function. Niobium is a metal with a body-centered cubic structure. The length of the unit cell structure is b = 0.3349 nm. (a) Find the volume for a unit cell structure for niobium. (b) There are 2 atoms per unit cell structure of niobium. The metal has a molar mass of 92.9 g / mol. One mole of the metal consists of 6.02 x 10 ^ 23 atoms. Find the mass of niobium per unit cell and the density of niobium.
- 1 Answers
- 2831 Views
- I also Faced
- E-Mail Answers
Answer Posted / kang chuen tat (malaysia - pen
Answer 48 - (a) V = 0.3349 x 0.3349 x 0.3349 = 0.0376 cubic nanometers. (b) Mass per unit cell = 2 x 92.9 (g / mol) [ 1 mol / (6.02 x 10 ^ 23 atoms) ] = 3.086 x 10 ^ (-22) g = m. V = 0.0376 x [ 10 ^ (-7) ] ^ 3 = 0.0376 x 10 ^ (-21) cubic cm. Then density is m / V = 8.207 g / cubic cm. The answer is given by Kang Chuen Tat; PO Box 6263, Dandenong, Victoria VIC 3175, Australia; SMS +61405421706; chuentat@hotmail.com; http://kangchuentat.wordpress.com.
| Is This Answer Correct ? | 0 Yes | 0 No |
Post New Answer View All Answers
print a pattern of abcdcba abc cba ab ba a a ab ba abc cba abcdcba
how much maximum power can be generated by 320v, 10kg-cm synchronus motor if shaft is roteted mechanically at 50 to 60 rpm?
What is the difference between cfm (cubic feet per minute) and scfm (standard cubic feet per minute)?
Explain what are the disadvantages of using gear pumps?
Explain what is the significance of the minimum flow required by a pump?
What are the methods involved to test helium leak testing in a vacuum system?
Calculate the line size for a cooling water line with a volumetric flowrate of 1200m3/h of water. Density of water = 1000kg/m3
What are some good tank mixing rules of thumb?
Explain the some guidelines for sizing a psv for a fire scenario on a vessel in a refinery service?
i am going to appear vedanta written test so plz can any body suggest me for this on madhu.5393@gmail.com
Why do we apply on iron articles?
What are the types of load?
hai....i am chandrika. if anybody having test questions for HAL,HPCL,ONGC,IOL...PLS SEND THE QUES WITH SOLVED ANSWERS TO ME TO MY MAIL ID chandrismiles@yahoo.co.uk
What is a good method of analyzing powders for composition?
Explain global warming from a common man's and an engineer's perspective?